HNA-200

MATERIAL COMPOSITION:

Made from ARAMID / CELLULOSE Fiber with mineral fibre and inorganic bonded with
synthetic NBR Elastomers.

APPLICATIONS:

Suitable for drinking water, approved NSF USA.

For light to medium loadings, suitable for low operating pressure, e.g. transformers, compressors,
valve cover and oil pans internal combustion engines

Diagram

Technical Specifications:

Properties	Test Method	Unit	Specified Value
Density		gm/cm³	1.70-2.00
Tensile Strength
(a) ACC to ASTM F 152 (Across Grain)		N/mm²	>8
(b) ACC to DIN 52910 (Across Grain)		N/mm²	>5
Compressibility	ASTM F36A	%	7-15
Recovery	ASTM F36A	%	>50
Fluid Absorption	ASTM F146
(a) In ASTM Oil No. 3 Increase in Mass Increase in Thickness		% %	<15 <10
(b) In Fuel B Increase in Mass Increase in Thickness	ASTM F146	% %	<10 <10
(c) In Water/Antifreeze Increase in Mass Increase in Thickness	ASTM F146	% %	<15 <15
Ignition Loss	DIN 52911	%	<35
Sealability Against Nitrogen	DIN 3535	CM³/min	<1.0
Stress Resistance			–
16h 300 ^oC	DIN 52913	N/mm²	–
16h 175 ^oC	DIN 52913	N/mm²	–
Max. Peak Temperature		^oC	300
Max. Continuous Temperature		^oC	220
Max. Operating Pressure		Kg/CM²	100

NOTE:

Graphite coating, teflon coating, antistick coating are also available on request. Properties applicable for 2.0mm thick material

NON - ASBESTOS JOINTING SHEETS

HNA-200

MATERIAL COMPOSITION:

APPLICATIONS:

Suitable for drinking water, approved NSF USA.

Diagram

NOTE:

Need support or have any inquiries?

Charminar Jointings Pvt. Ltd.

Phone

Email

Important Links